Effects of Cover Sheets on the Nugget Growth and Fracture Behavior of Resistance Spot Welded Q&P980 Steel Joints
文献摘要:
The resistance spot weldability of galvanized ultra-high-strength steels is not satisfied,the joints are prone to interfa-cial fracture and the weldable current range is narrow.To solve the problems,a novel method called resistance spot welding with double-sided cover sheets was introduced to weld a galvanized Q&P980 steel with the thickness of 1.2 mm.Two thin SPCC mild steel sheets were chosen as cover sheets and were placed symmetrically at both sides between the Q&P980 steels and the electrodes,then the RSW process was carried out.Compared with the traditional RSW method,the joints obtained by using the novel method achieved larger tensile shear strength and energy absorption,which increased by 26.9%and 52.6%,respectively.With increasing the welding current,the failure mode transferred from interfacial fracture to nugget pull-out fracture or base metal tearing fracture.By contrast,the joints always showed interfacial fracture without cover sheets.The improvement of the joint performance was mainly attrib-uted to the enlargement of the nugget.With the help of finite element simulation,it was found that the cover sheets helped increase the contact area and reduced the current density during welding,which postponed the expulsion,and a larger area could be evenly heated.The application of the novel method can be easily extended to the resist-ance spot welding of other ultra-high-strength steels with various thicknesses.
文献关键词:
作者姓名:
Zhanxiang Ling;Ting Chen;Liang Kong;Min Wang
作者机构:
Shanghai Key Laboratory of Materials Laser Processing and Modification,Shanghai Jiao Tong University,Shanghai 200240,China
引用格式:
[1]Zhanxiang Ling;Ting Chen;Liang Kong;Min Wang-.Effects of Cover Sheets on the Nugget Growth and Fracture Behavior of Resistance Spot Welded Q&P980 Steel Joints)[J].中国机械工程学报,2022(04):192-205
A类:
Nugget,weldable
B类:
Effects,Cover,Sheets,Growth,Fracture,Behavior,Resistance,Spot,Welded,P980,Steel,Joints,resistance,spot,weldability,galvanized,ultra,high,strength,steels,not,satisfied,joints,prone,fracture,current,range,narrow,To,solve,problems,novel,method,called,welding,double,sided,cover,sheets,was,introduced,Two,thin,SPCC,mild,were,chosen,placed,symmetrically,both,sides,between,electrodes,then,RSW,process,carried,Compared,traditional,obtained,by,using,achieved,larger,tensile,shear,energy,absorption,which,increased,respectively,With,increasing,failure,mode,transferred,from,interfacial,nugget,pull,base,metal,tearing,By,contrast,always,showed,without,improvement,performance,mainly,attrib,uted,enlargement,finite,element,simulation,found,that,helped,contact,area,reduced,density,during,postponed,expulsion,could,evenly,heated,application,can,easily,extended,other,various,thicknesses
AB值:
0.55371
相似文献
机标中图分类号,由域田数据科技根据网络公开资料自动分析生成,仅供学习研究参考。