High cycle rotating bending fatigue performance and fracture behavior in a pearlite-ferrite dual-phase steel
文献摘要：
To clarify the effects of ferrite morphologies and contents on high-cycle fatigue property of pearlite-ferrite dual-phase(DP)steel used for fabrication of commercial vehicle crankshafts,two types of DP steels with different ferrite grain sizes(S10:13.1 μm and S30:21.4 μm)and ferrite contents(S10:～9.5 vol.％and S30:～30.4 vol.％)were prepared.Stress amplitude-logarithm of number of high cycles to failure fatigue of the two DP steels was evaluated.Experimental results showed a fatigue strength of 510 and 400 MPa for S10 and S30 steels,respectively,at 107 cycles.Fatigue cracks in S10 steel extended preferentially along the grain boundary,but it was easy for crack propagation to extend within a pearlite colony to form a zigzag crack morphology.Crack roughness was enhanced and high stress was introduced to the crack surface due to this kind of crack propagation behavior,which has positive effects on slowing down crack propagation.However,the crack propagation in S30 steel mainly occurred inside the soft equiaxed coarse ferrite grain.Analysis revealed that little stress was introduced to the crack surface.These results show that it is possible to improve high cycle fatigue strength of pearlite-ferrite DP steel by appropriately manipulating the volume fraction and microstructure mor-phology of ferrite phase.
文献关键词：
中图分类号：
作者姓名：
Xin-bo Ji;Si-xin Zhao;Li-ming Fu;Jian Peng;Jia-qiang Gao;Da-jiang Yu;Zong-ze Huang;Ai-dang Shan
作者机构：
School of Materials Science and Engineering,Shanghai Jiao Tong University,Shanghai 200240,China;Baosteel Research Institute,Baoshan Iron and Steel Co.,Ltd.,Shanghai 201900,China
文献出处：
引用格式：
[1]Xin-bo Ji;Si-xin Zhao;Li-ming Fu;Jian Peng;Jia-qiang Gao;Da-jiang Yu;Zong-ze Huang;Ai-dang Shan-.High cycle rotating bending fatigue performance and fracture behavior in a pearlite-ferrite dual-phase steel)[J].钢铁研究学报（英文版）,2022(03):519-528
A类：
crankshafts
B类：
High,rotating,bending,fatigue,performance,fracture,behavior,pearlite,ferrite,dual,phase,To,clarify,effects,morphologies,contents,high,property,DP,used,fabrication,commercial,vehicle,two,types,steels,different,grain,sizes,S10,S30,were,prepared,Stress,amplitude,logarithm,number,cycles,failure,was,evaluated,Experimental,results,showed,strength,respectively,Fatigue,cracks,extended,preferentially,along,boundary,but,easy,propagation,within,colony,zigzag,morphology,Crack,roughness,enhanced,stress,introduced,surface,due,this,kind,which,positive,slowing,down,However,mainly,occurred,inside,soft,equiaxed,coarse,Analysis,revealed,that,little,These,possible,improve,by,appropriately,manipulating,volume,fraction,microstructure
AB值：
0.465085
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。