Evolution of grain size and grain shape during thermomechanical processing in a powder metallurgical nickel-based superalloy
文献摘要：
With a strain rate range of 0.01-10 s-1and a deformation temperature range of 1110-1200℃,the isothermal compression test was performed on one powder metallurgy superalloy which is macroscopic segregation free.Using electron backscatter diffraction,the effect of strain rate and deformation temperature on grain shape and grain size of superalloys during thermal deformation was studied.The results established that exquisite and equiaxed dynamic recrystallization(DRX)grains are procured at supernal deformation temperature and high strain rate because of the high dislocation density.At the same time,the interaction between high DRX nucleation rate and low grain growth rate at high strain rate is favorable in making finer DRX grains.The equivalent medial grain size expanded with lowering strain rate and elevating proof temperature.Moreover,the grain shape was researched by the effective method of aspect ratio.Most aspect ratio of original grains is 0.61,and the aspect ratio has important implications for DRX and grain growth process.The average aspect ratio increases slightly when deformation temperature rises from 1110 to 1140℃,while the average aspect ratio increases memorably as the deformation temperature is higher than 1140℃.
文献关键词：
中图分类号：
作者姓名：
Yan-hui Liu;Zhao-zhao Liu;Miao Wang
作者机构：
College of Mechanical and Electrical Engineering,Shaanxi University of Science and Technology,Xi'an 710021,Shaanxi,China;School of Materials Science and Engineering,Northwestern Polytechnical University,Xi'an 710072,Shaanxi,China;Zhejiang Wenzhou Research Institute of Light Inousty,Wenzhou 325002,Zhejiang,China
文献出处：
引用格式：
[1]Yan-hui Liu;Zhao-zhao Liu;Miao Wang-.Evolution of grain size and grain shape during thermomechanical processing in a powder metallurgical nickel-based superalloy)[J].钢铁研究学报（英文版）,2022(02):350-358
A类：
supernal,memorably
B类：
Evolution,size,shape,during,thermomechanical,processing,powder,metallurgical,nickel,With,strain,rate,range,1and,deformation,temperature,isothermal,compression,test,was,performed,one,metallurgy,which,macroscopic,segregation,free,Using,electron,backscatter,diffraction,superalloys,studied,results,established,that,exquisite,equiaxed,dynamic,recrystallization,DRX,grains,are,procured,because,dislocation,density,At,same,interaction,between,nucleation,growth,favorable,making,finer,equivalent,medial,expanded,lowering,elevating,proof,Moreover,researched,by,effective,method,aspect,ratio,Most,original,has,important,implications,average,increases,slightly,when,rises,from,while,higher,than
AB值：
0.501633
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。