Preparation of Lead-free Base Glaze Suitable for Pearlescent Pigments by Low-temperature Solid-phase Reaction with Alkali Waste
文献摘要：
A lead-free base glaze suitable for pearlescent pigments was prepared by a low-temperature solid-phase reaction with alkali waste. Tests were performed to evaluate the effects of the sintering conditions and alkali waste composition on the prepared base glaze and pearlescent glaze. The experimental results show that partially replacing SiO2 with B2O3 effectively reduced the sintering temperature and time to form a glass network, but the network structure becomes disconnected as the B2O3 content increases. An amorphous base glaze was obtained when soda ash was replaced with a small amount of alkali waste, but increasing the addition of NaCl further was adverse to base glaze formation by resulting in crystallization of the base glaze and a decrease in the bridging oxygen content. The pearlescent pigment was thermally stable in the glaze at 750 ℃, while higher temperatures caused the crystalline phase of NaAlSiO4 to appear and adhere to the surface of pigment granules, which degraded the pearlescent effect of the glaze.
文献关键词：
中图分类号：
作者姓名：
RAO Li;HUANG Kang;FU Qiong;WANG Junwei;DAI Li;ZHAO Na;LI Xiangjun;HE Yong;ZHOU Yi;CHEN Yanlin
作者机构：
College of Materials and Chemical Engineering,Hubei University of Technology,Wuhan 430068,China;Hubei Provincial Key Labo-ratory of Green Materials for Light Industry,Hubei University of Technology,Wuhan 430068,China;New Materials and Green Manufac-turing Talent Introduction and Innovation Demonstration Base,Hubei University of Technology,Wuhan 430068,China;Hubei Longzhong Laboratory,Xiangyang 441000,China
文献出处：
引用格式：
[1]RAO Li;HUANG Kang;FU Qiong;WANG Junwei;DAI Li;ZHAO Na;LI Xiangjun;HE Yong;ZHOU Yi;CHEN Yanlin-.Preparation of Lead-free Base Glaze Suitable for Pearlescent Pigments by Low-temperature Solid-phase Reaction with Alkali Waste)[J].武汉理工大学学报（材料科学版）（英文版）,2022(06):1262-1270
A类：
Glaze,Pearlescent,pearlescent
B类：
Preparation,Lead,free,Base,Suitable,Pigments,by,Low,Solid,phase,Reaction,Alkali,Waste,lead,base,glaze,suitable,pigments,prepared,low,solid,reaction,alkali,waste,Tests,were,performed,evaluate,effects,sintering,conditions,composition,experimental,results,show,that,partially,replacing,SiO2,B2O3,effectively,reduced,glass,network,but,structure,becomes,disconnected,content,increases,An,amorphous,obtained,when,soda,ash,replaced,small,amount,increasing,addition,NaCl,further,adverse,formation,resulting,crystallization,decrease,bridging,oxygen,thermally,stable,while,higher,temperatures,caused,crystalline,NaAlSiO4,appear,adhere,surface,granules,which,degraded
AB值：
0.536988
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。