Effect of Al content on the reaction between Fe?10Mn?xAl (x = 0.035wt％, 0.5wt％, 1wt％, and 2wt％) steel and CaO?SiO2?Al2O3?MgO slag
文献摘要：
The effect of Al content (0.035wt％, 0.5wt％, 1wt％, and 2wt％) on the composition change of steel and slag as well as inclusion transformation of high manganese steel after it has equilibrated with CaO?SiO2?Al2O3?MgO slag was studied using the method of slag/steel reaction. The experimental results showed that as the initial content of Al increased from 0.035wt％ to 2wt％, Al gradually replaced Mn to re-act with SiO2 in slag to avoid the loss of Mn due to the reaction; this process caused both Al2O3 in slag and Si in steel to increase while SiO2 and MnO in slag to reduce. In addition, the type of inclusions also evolved as the initial Al content increased. The evolution route of inclusions was MnO → MnO?Al2O3?MgO → MgO → MnO?CaO?Al2O3?MgO and MnO?CaO?MgO. The shape of inclusions evolved from spheric-al to irregular, became faceted, and finally transformed to spherical. The average size of inclusions presented a trend that was increasing first and then decreasing. The transformation mechanism of inclusions was explored. As the initial content of Al increased, Mg and Ca were re-duced from top slag into molten steel in sequence, which consequently caused the transformation of inclusions.
文献关键词：
中图分类号：
作者姓名：
Huixiang Yu;Dexin Yang;Jiaming Zhang;Guangyuan Qiu;Ni Zhang
作者机构：
School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China
文献出处：
引用格式：
[1]Huixiang Yu;Dexin Yang;Jiaming Zhang;Guangyuan Qiu;Ni Zhang-.Effect of Al content on the reaction between Fe?10Mn?xAl (x = 0.035wt％, 0.5wt％, 1wt％, and 2wt％) steel and CaO?SiO2?Al2O3?MgO slag)[J].矿物冶金与材料学报,2022(02):256-262
A类：
035wt
B类：
Effect,content,reaction,between,10Mn,xAl,1wt,2wt,steel,CaO,SiO2,Al2O3,MgO,slag,effect,composition,change,well,transformation,high,manganese,after,has,equilibrated,was,studied,using,method,experimental,results,showed,that,initial,increased,from,gradually,replaced,avoid,loss,due,this,process,caused,both,while,MnO,reduce,In,addition,type,inclusions,also,evolved,evolution,route,shape,irregular,became,faceted,finally,transformed,spherical,average,size,presented,trend,increasing,first,then,decreasing,mechanism,explored,were,duced,top,into,molten,sequence,which,consequently
AB值：
0.405773
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。