Microstructure and phase elemental distribution in high-boron multi-component cast irons
文献摘要：
The novel cast irons of chemical composition (wt％) 0.7C–5W–5Mo–5V–10Cr–2.5Ti were invented with the additions of 1.6wt％ B and 2.7wt％ B. The aim of this work was to study the effect of boron on the structural state of the alloys and phase elemental distribution with respect to the formation of wear-resistant structural constituents. It was found that the alloy containing 1.6wt％ B was composed of three eu-tectics: (a) "M2(C,B)5+ferrite" having a "Chinese Script" morphology (89.8vol％), (b) "M7(C,B)3+Austenite" having a "Rosette" morphology, and (c) "M3C+Austenite" having a "Ledeburite"-shaped morphology (2.7vol％). With 2.7wt％ of boron content, the bulk hardness increased from HRC 31 to HRC 38.5. The primary carboborides M2(C,B)5 with average microhardness of HV 2797 appeared in the structure with a volume fraction of 17.6vol％. The volume fraction of eutectics (a) and (b, c) decreased to 71.2vol％ and 3.9vol％, respectively. The matrix was"ferrite/austenite" for 1.6wt％ B and "ferrite/pearlite" for 2.7wt％ B. Both cast irons contained compact precipitates of carbide (Ti,M)C and car-boboride (Ti,M)(C,В) with a volume fraction of 7.3％–7.5％. Based on the energy-dispersive X-ray spectroscopy, the elemental phase distribu-tions and the appropriate phase formulas are presented in this work.
文献关键词：
中图分类号：
作者姓名：
Yu.G.Chabak;K.Shimizu;V.G.Efremenko;M.A.Golinskyi;K.Kusumoto;V.I.Zurnadzhy;A.V.Efremenko
作者机构：
Physics Department,Pryazovskyi State Technical University,Mariupol,87555,Ukraine;Mechanical Engineering Research Unit,College of Design and Manufacturing Technology,Muroran Institute of Technology,Muroran-city,050-8585,Japan
文献出处：
引用格式：
[1]Yu.G.Chabak;K.Shimizu;V.G.Efremenko;M.A.Golinskyi;K.Kusumoto;V.I.Zurnadzhy;A.V.Efremenko-.Microstructure and phase elemental distribution in high-boron multi-component cast irons)[J].矿物冶金与材料学报,2022(01):78-87
A类：
tectics,5+ferrite,8vol,3+Austenite,Rosette,M3C+Austenite,Ledeburite,7vol,carboborides,6vol,9vol,boboride
B类：
Microstructure,phase,elemental,distribution,high,boron,multi,component,cast,irons,novel,chemical,composition,7C,5W,5Mo,5V,10Cr,5Ti,were,invented,additions,6wt,7wt,aim,this,work,was,study,effect,structural,state,alloys,formation,wear,resistant,constituents,It,found,that,containing,composed,three,M2,having,Chinese,Script,morphology,M7,shaped,With,content,bulk,increased,from,HRC,primary,average,microhardness,HV,appeared,volume,fraction,eutectics,decreased,2vol,respectively,matrix,austenite,pearlite,Both,contained,compact,precipitates,carbide,Based,energy,dispersive,ray,spectroscopy,appropriate,formulas,presented
AB值：
0.474415
相似文献
机标中图分类号，由域田数据科技根据网络公开资料自动分析生成，仅供学习研究参考。